PELAPISAN GALVANIS PENCELUPAN BESI/BAJA (BERSIH) + BEBAS OKSIGEN KE DLM. LEBURAN SENG. BERTUJUAN MEMBENTUK LAPISAN SENG (METALURGI) TERIKAT KE PERMUKAAN BESI (BAJA). LAPISAN SENG MELINDUNGI PERMUKAAN DARI KOROSI DNG. CARA : 1. MENUTUPI LOGAM DASAR DARI ATMOSFIR 2. SENG MEMBERIKAN PERLINDUNGAN KATODIK (BESI/BAJA MENGANDUNG ELEKTRONEGATIF). 1



GALVANIS CELUP PANAS MUDAH DIAPLIKASI MELAPISI HAMPIR SEMUA TIPE PRODUK BUATAN ATAU NON BUATAN SEPERTI KABEL,TANGKI,LEMBARAN,PIPA , TABUNG, PEMBUNGKUS KAWAT,RAKITAN STRUKTUR. LANGKAH PENTING GALVANISASI : 1. PERSIAPAN PERMUKAAN 2. PREFLUXING 3. GALVANISASI 4. PENYEMPURNAAN



2



SPESIFIKASI ASTM METALPLATE AKAN DIGALVANISASI : A-123 : ZINC (HOT GALVANIZED) COATING ON IRON & STEEL PRODUCTS. A-143 : SAFEGUARDING AGAINST EMBRITTLEMENT OF HOT-DIP GALVANIZED STRUCTURAL STEEL PRODUCT FOR DETECTING EMBRITTLEMENT A-153 : ZINC COATING (HOT DIP) ON IRON & STEEL HARDWARE. A-384 : SAFEGUARDING AGAINST WARPAGE & DISTORTION DURING HOT DIP GALVANIZING OF STEEL ASSEMBLIES. A-385 : PROVIDING HIGH QUALITY ZINC COATING (HOT DIP) ON ASSEBLED PRODUCT.



3



A-780 :



STANDARD PRACTICE FOR REPAIR OF DAMAGED HOT DIP GALVANIZED COATINGS.



KEUNTUNGAN GALVANISASI : 1. BIAYA AWAL RENDAH 2. PERAWATAN MINIM/BIAYA JANGKA PANJANG RENDAH 3. USIA PANJANG 4. KEHANDALAN CUKUP BAIK 5. LAPISAN TERKUAT 6. PERLINDUNGAN OTOMATIS UNTUK BAGIAN YANG RUSAK 7. PERLINDUNGAN LENGKAP



4



8. INSPEKSI MUDAH 9. WAKTU PROSES CEPAT. LAPISAN PENAMPANG HASIL (PHOTOMICROGRAPH): 1. BASE STEEL 2. GAMMA LAYER 75%Zn,25% Fe 3. DELTA LAYER 90% Zn,10% Fe 4. ZETA LAYER 94% Zn, 6% Fe 5. ETA LAYER 100%



GALVANISASI



5