Aisi 1015 Steel [PDF]

Citation preview

AISI 1015 Steel, cold drawn Categories: Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon Steel The composition listed is only for structural shapes, plate, sheet, strip, and welded Material tubing. Hot-rolled and cold finished bars, semifinished products for forging, wire Notes: rods, and seamless tubing have a carbon content of 0.13 - 0.18%. Has better machinability and carburizing characteristics than the more formable extra-low carbon steels. Applications: cold-formed, cold-headed, or forged parts which are low strength with hard, wear resistant surfaces. Key Words: UNS G10150 No vendors are listed for this material. Please click here if you are a supplier and Vendors: would like information on how to add your listing to this material. Physical Properties Metric Density 7.87 g/cc Mechanical Properties Hardness, Brinell 111 Hardness, Knoop 129 Hardness, Rockwell B 64



English 0.284 lb/in³



Comments



English



Comments



Metric 111 129 64



Hardness, Vickers



115



115



Tensile Strength, Ultimate Tensile Strength, Yield Elongation at Break Reduction of Area Modulus of Elasticity Bulk Modulus Poissons Ratio Machinability



385 MPa



55800 psi



325 MPa



47100 psi



18 % 40 % 205 GPa 160 GPa 0.29 60 %



18 % 40 % 29700 ksi 23200 ksi 0.29 60 %



Shear Modulus



80.0 GPa



11600 ksi



Converted from Brinell hardness. Converted from Brinell hardness.



In 50 mm Typical for steel Typical for steel Typical For Steel Based on 100% machinability for AISI 1212 steel. Typical for steel



Electrical Properties Metric English Comments Electrical Resistivity 0.0000159 ohm-cm 0.0000159 ohm-cm annealed condition @Temperature 0.000 @Temperature 32.0



°C 0.0000219 ohm-cm @Temperature 100 °C 0.0000292 ohm-cm @Temperature 200 °C Thermal Properties Metric CTE, linear 11.9 µm/m-°C @Temperature 0.000 - 100 °C 13.0 µm/m-°C @Temperature 0.000 - 300 °C 14.2 µm/m-°C @Temperature 0.000 - 500 °C Specific Heat 0.486 J/g-°C Capacity @Temperature >=100 °C Thermal Conductivity 51.9 W/m-K



Component Elements Metric Properties Carbon, C 0.13 - 0.18 % Iron, Fe 99.13 - 99.57 % Manganese, Mn 0.30 - 0.60 % Phosphorous, P