AISI 1020 Steel, cold rolled Categories:



Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon Steel



Material Notes:



1020 steel responds well to cold work and heat treating. Weldability is fair. Applications: Shafts, lightly stressed gears, hard wearing surfaces, pins, chains and case hardened parts where core strength is not critical. 1020 is suitable for case hardened parts where core strength is not critical.



Key Words:



UNS G10200, AMS 5032, AMS 5045, ASTM A29, ASTM A108, ASTM A510, ASTM A519, ASTM A29, A108, A510, A512, A513, A519, A544, A575 M10120, A576, A635, A659, A827, A830, BS 970 040A20, 050A20 (En2C), 050A20 (En2D), 060A20, BS 970 Part 1 070M20, DEF STAN95-1-1 C1020, SAE J412, SAE J414, DIN 1.0402, AFNOR CC 20, UNI C 20, SS14 1450 (Sweden), SAE J403



Vendors:



Click here to view all available suppliers for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.



  Physical Properties Density   Mechanical Properties Hardness, Brinell Hardness, Knoop Hardness, Rockwell B Hardness, Vickers Tensile Strength, Ultimate Tensile Strength, Yield Elongation at Break Reduction of Area Modulus of Elasticity Bulk Modulus Poissons Ratio Machinability Shear Modulus   Electrical Properties Electrical Resistivity       Thermal Properties CTE, linear 20°C CTE, linear 250°C CTE, linear 500°C Specific Heat Capacity     Thermal Conductivity   Material Components Properties Carbon, C Iron, Fe Manganese, Mn Phosphorous, P Sulfur, S



Metric 7.87 g/cc



English 0.284 lb/in³



Comments



Metric 121 140 68.0 126 420 MPa 350 MPa 15.0 % 40.0 % 205 GPa 140 GPa 0.290 65.0 % 80.0 GPa



English 121 140 68.0 126 60900 psi 50800 psi 15.0 % 40.0 % 29700 ksi 20300 ksi 0.290 65.0 % 11600 ksi



Comments



Based on AISI 1212 steel. as 100% machinability Typical for steel



Metric 0.0000159 ohm-cm 0.0000219 ohm-cm



English 0.0000159 ohm-cm 0.0000219 ohm-cm



Comments condition unknown; 0°C (32°F) condition unknown



@Temperature 100 °C



@Temperature 212 °F



0.0000292 ohm-cm



0.0000292 ohm-cm



@Temperature 200 °C



@Temperature 392 °F



Metric 11.7 µm/m-°C 12.8 µm/m-°C 13.9 µm/m-°C 0.486 J/g-°C 0.519 J/g-°C



English 6.50 µin/in-°F 7.11 µin/in-°F 7.72 µin/in-°F 0.116 BTU/lb-°F 0.124 BTU/lb-°F



@Temperature 150 - 200 °C



@Temperature 302 - 392 °F



Converted from Brinell hardness. Converted from Brinell hardness. Converted from Brinell hardness.



In 50 mm Typical for steel Typical for steel



condition unknown



Comments 0-100ºC 0-300°C (68-570°F) 0-500°C (68-930°F) condition unknown; 50-100°C (122-212°F)



0.599 J/g-°C



0.143 BTU/lb-°F



@Temperature 350 - 400 °C



@Temperature 662 - 752 °F



51.9 W/m-K



360 BTU-in/hr-ft²-°F



Typical steel



Metric 0.170 - 0.230 % 99.08 - 99.53 % 0.300 - 0.600 %